Double component waterproofing
coating belongs to solidify waterproof materials, and the
Group A is isocyanate terminated pre-polymer polycondensated by
polyether and isocyanate, Group B is colored liquid composed of
plasticizer, curing agent, thickening agents, coagulant agent and
filler, Mix Group A and B evenly as rate and brush on the
waterproofing substrate surface, form a elastisic and rubber-like
coating film through cross-linking and solidifying at
normal temperature , which plays a role
of waterproofing.
Double component waterproofing coating
forms seamless, integrate elasticity waterproof layer after
solidifying, and improve waterproof and seeping resistance of the
project, which is waterproof membrane that can not be attained.
Especially the coating film has high elasticity and elongation ,
high adaptability to substrate craking or expansion.
Firm bonding with substrate , coating
film has extreme bonding power with concrete, timber, metal,
pottery and asbestos shingle, also can be used as bond.
Convenient application ,polyurethane coating film is a cold
application waterproof coating ,just mix group A and B as rate
when application and brush it on the waterproof substrate
.
Easy maintenance ,only maintain the
broken parts ,which can reach the original effects of
waterproofing ,save time ,save power and low cost .
Environmental product, and reduce the
damage to the people and environment..
Main
features:
High elasticity and extensibility of film forming,
seamless
weather resistance, acid alkali
resistance and strong adhesive properties
high performance of waterproofing and ageing resistance
Environmental protecting
product
1)Two units, mixed in construction
locate.
2)Could be colorful.
3)After curing, the membrane has high
strength and elongation , it has good adaptability to fit for the
foundation crack and the extension. The service life of the
product is *5 years.
The product is suitable for roofing,
basement, toilet, swimming pool, etc.
4)Basement treatment:
Waterproofing base shall be strong,
smooth and clean without particles on the surface. No peeling or
cracking shall exist at the surface. The corners of the base
shall be made into arcs with a radius of no less than *0mm or
triangular. The drain slope, division seam, and air vent shall be
carried out and treated according to design requirements.
Installation:
Make primer: Mix DPU and solvent by
A:B:Solvent=1:2:1, then brush primer on the foundation until it
is Mix A:B=1:2. Scratch the coating by 3 times. The first
layer curing needs ****4 hours. When the first layer is
solidifying, do the second layer. The direction of the second
layer should be at right angles to the first layer. Then repeat
the third one. If add protective layer, before the third layer is
cured, scatter clean sand on its surface. After the membrane is
cure, can begin the protective layer construction.
Product Specification:
|
Type
|
Double-component Polyurethane
Waterproof Coating
|
|
|
Material
|
polyether and Isocyanate;
Colored Liquid
|
|
Thickness
|
1.5mm*2.0mm
|
|
Density
|
1.**1.5Kg/sqm while
thickenss is1mm.
|
|
Usage
|
basements,Building
Coating, Road Marking Paint, Rubber Coating, Other
|
|
Application
Method
|
Brush
|
|
Packing
|
Plastic
Barrel, Pallet
|
|
Loading in
Container
|
TBA
|
|
Colors
|
Customized
|
|
Enclosure
|
NONE
|
| 国: |
China |
| モデル番号: |
Double component
|
| 离岸价格: |
（交渉可能）
Get Latest Price
|
| ロケーション: |
China |
| 最低注文量の価格: |
- |
| 最低注文量: |
3 Ton |
| パッケージの詳細: |
20kg/barrel |
| 納期: |
10days |
| 供給能力: |
3 Ton per Day |
| 支払いタイプ: |
L/C, T/T |
| 製品グループ : |
- |