Properties

ASTM method

Test Condition

Unit

Typical Value

Specific Gravity

D**2

**-

**-

1.**6

Melt Flow Index

D***8

**0°C,5 kg load

g/*0 min

4.6

Tensile Strength at Yield

D**8

*3°C,1/8” Sample

kg/cm2

**0

Elongation at Break

D**8

*3°C,1/8” Sample

%

*0

Izod Impact Strength

D**6

*3°C,A method,notched1/8”×1/2”×5/2”

kg/m2

9.5

Vicat Softening Temperature

D***5

1 kg load,3 mm Thick ( **0°C/hr )

°C

*7

Flammability

UL**4

1/*6” Sample

File No.E****3

*4HB

Residual SM monomer

**-

**-

ppm

<**0

Yellow Index

**-

**-

**-

*6

Performance of Projects 

Test condition

Testing Method

Test Data

Data Unit

Others

Bending modulus

**-

ASTM D***0

2.3(***0)

kg/cm2×**4(MPa)

Basic  Properties

Melt Flow Index

**-

ASTM D****8

5.5

g/*0min

Mechanical  Properties

IZOD impact strength

**-

ASTM D***6

*1.0(**8)

kg-cm/cm(J/m)

Tensile strength

**-

ASTM D***8

**0(*2)

kg/cm2(MPa)

Tensile modulus

**-

ASTM D***8

1.5(***0)

kg/cm2×**4(MPa)

elongation

**-

ASTM D***8

*0

%

Bending strength

**-

ASTM D***0

**0(*3)

kg/cm2(MPa)

Thermal  Properties

Vicat Softening

 point

**-

ASTM D****5

*5

°C

Heat distortin temperature

**-

ASTM D****5

*8

°C

Other

Residucl monomer

**-

**-

**0

ppm max

Burning rate

1/*6"

UL *4

NC

HB