Rubber raw material silicon

タイトルまたは説明

Specifications of Liquid Silicone Rubber for Soap Mold Making

1. Good flow ability and long working time
2. Low hardness, easy de-mold
3. High tear and tensile strength
4. Acid and alkali-resistance
5. Low linear shrinkage



 
Procedures
1. Make sure the surface of the original is clean and free of loose material. 
2. Weight **0 Part A base and 2 parts of CA*0 Curing Agent in a clean container.
3. Stir Part A base silicone before use thoroughly , as filler separation may occur upon prolonged storage.
4. Mix Part A and Part B evenly until the CA*0 completely dispersed in the base. 
5. Pour the mixed Part A base silicone and CA**0 curing agent as soon as possible onto the original
6. De-mold after *4 hours ,it is will improve the replicate times of silicone mold.
Note:It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further **2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of **5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.