Silicon carbide ceramic foam filters of NINGXIN are designed to improve the quality of nodular,grey,and malleable iron castings. The filter can effectively remove non-metallic inclusions including slag and dross from the molten metal stream. Additionally, they aid in reducing turbulence in the gating system. Ningxin ceramic foam filter's outstanding thermal shock resistance and high strength properties were developed for superior performance in extreme iron foundry applications.

-Clean iron castings
-Increased casting yield
-Fewer inclusions
-Real cost savings from significant
-Consistent pour times

Mode:NX-PTW-T
Products confirm with China National Standard GB/T *********0.

Technical Data
Material:Silicon Carbide
Aplied Temp:≤***0 Degree C 
Color:Gray-black
Hole density (PPI):****0(PPI=pore per inch)
Porosity(%):****0
Bending stength(Mpa):0.8
Compressive Strength(MPa):≥1.0
Bulk Density(g/cm3):0.***0.*0
Thermal shock resistance:6times/***0 Degree C    
High temperature bending strength(***0Degree C)MPa:≥0.4
Application:Molten Iron,copper and alloy

Common specification
Round shape:
*0x*1mm, *0x*5mm, *0x*5mm, *0x*0mm, *0x*2mm, *0x*2mm, *0x*2mm , *0x*2mm,**0x*2mm, **5x*5mm
Square shape:
*0x*0x*1mm, *0x*0x*5mm, *0x*0x*2mm, *5x*5x*2mm, *0x*5x*2mm, **0x*5x*2mm, **0x**0x*2mm, *5x*5x*5mm, **0x**0x*2mm

Varies of shape,size and PPI are available as per request.

Chemical Composition

Al2O3       SiC       SiO2         Fe2O3
≤*8.*0%      ≥*2.*0%    ≤*0.*0%     ≤0.*0%