タイトルまたは説明

LLDPE Virgin granules off grade/ powder LLDPE 
1, LLDPE film grade
Tests          Value      Unit
Melt Flow Rate: 2.0±0.4g/10min
Density :920±2Kg/cm3
Tensile Strengthat Yield:8Mpa ≥
Tensile Strengthat Break:12Mpa
haze:15%≤
Packing: In 25 kg PP woven bags,20MT/20FCL

1. HDPE High Density Polyethylene materials 
2.virgin/recycle HDPE
Mass density 0.941-0.959g/cm 3
Melt flow Rate(190 centidegree /2.16kg) ≤1.0g/10min
Tensile yield strength ≥19.0MPa
Flexural modulus ≥* *@********************mpact Embrittlement temperature MAX -118centidegree

1.Low Density Polyethylene LDPE granules 
2.Virgin & Recycled 
Grade:  
 1. Blow molding grade,
 2. Injection molding grade,
 3. Film grade;
 4. Extrusion grade.

Specification :
LDPE Injection Grade
Tests                                         Value                     
Melt Flow Rate (MFR)          15g/10min
Density                                   0.922 g/cm3
Tensile Yield   Strength          7 Mpa
Elongation at Break               75 %
Wien Softening   Point           85°C
Packing        In 25 kg PP woven bags,20MT/20FCL
 
ABS Plastic/ABS Granules/Recycled Grade Plastic ABSGranules 
High Liquidity/Flowability 
Character:
1) ABS is a high strength, good toughness, easy process forming of thermoplastic polymer material.
2) It is the graft copolymer of Acrylonitrile, Butadiene and Styrene.
3) ABS plastic molding temperature of 180-250 ° C, but preferably not more than 240 ° C, or resin will break down.
Details: 15% to 35% of acrylonitrile, 5% to 30% of butadiene, 40% ~ 60% of styrene,
the most common ratio is A: B: S = 20: 30: 50