Sell AAC block production line

Description

Advantage:
 
1. High cutting precision, the length and width tolerance of product can be controlled within 1mm.
 
 2. Cutting vibration distance can reach ****0mm, which can more easily cut to the cake bottom.
 
 3. After cutting, the block is pushed to the autoclave without waste slurry on six sides.
 
 4. The production rate is over *8%, which reduce the production cost.
 
 5. Double layer cakes in autoclave, which improve the production efficiency.
 
 6. High automatic, low manpower.
 
 7. No waste slurry, economic and environmental protection.

 
Pre-sales of fully-automated flyash/sand aac block production line for customers:
1. Based on customer's requirement, we select equipment type in the principle of "Best cost performance is reached with most economical investment".
2. Provide the most reasonable program and give necessary illustration till accordant with customer.
3. Through negotiation, technical engineer can be sent to scene for layout for customer.
 
Mid-salesof fully-automated flyash/sand aac block production line for customers: 1. Design the technical documents such as whole equipment layout, construction bases layout, equipment installation drawings based on the scene.
2. Produce the equipments strictly as the contract when the customer is doing base construction.
3. Inspection before delivery, shipment organization and customer take-over..
 
After-sales of fully-automated flyash/sand aac block production line for customers:
1. Technical engineer will be sent to scene for instruction, installation and test run.
2. On-spot training for customer operator after installation and debug.
3. Irregular return visit to customer after normal production begins.
 
Regarding the fully-automated flyash/sand aac block production line , we can supply all the equipments from ****0cbm*******0cbm3 with high quality and best service, we have rich experience in installing the fully-automated flyash/sand aac block production line abroad and helping our customers to operate it well. 
1.  SIMPLE INTRODUCE
      Areated concrete brick (light brick ) is the light and porous buidling material. It has light keeping temperature cant burn and other advantages.it can be made into many kinds of bricks(for example:**0×**0×**0,*0×*0×**0,**0×**5×*3,**0×**0×**5),they could be used industry building and common building.they are more and more popular in the world.in the future,they will replace the Clay brick completely.
 
 2.AUTOCLAVED AERATED CONCRETE COMMON CONCEPTION 
       Common concrete density is usually ********0kg/m3,but Areated concrete are **0kg/m3,**0kg/m3,**0kg/m3.It has not the big grain,main use silicon material (for example:coal ash,sand,stone dust and others ),through making the material small for example sand,they can be used directly if has enough degree of small (for example coal ash.Mixing  calcium material lime cement water to a special slop,then add the aluminum dust and the additive.Make the aluminum dust and the special slop have a Chemical reflect.then produce Hydrogen to make the concrete slop to expanding or swell,foam.Next,put them into the curing room to concreting cutting steaming curing,last,there will bacome the light brick,the porous rate is ****0%.
3.DETAILED PRODUCT DESCRIPTION
foam block machine,
aerated autoclaved concrete plant, AAC block,aac production line,aac plant,AAC brick,autoclave aerated concrete block,concrete block machine,light weight block
 
1        Product weight is according to **0kg/m3 to control.
2        annual capacity **0,**0M3.
3        set raw  material proportion: cement 6.5%, raw lime *3%, flyash *8%, gypsum 3%, aluminum paste powder **0g/M3.
4        water and material rate 0.**1
5        one mould product 2.*8M3
6        Casting slurry cycle time **6 minutes, cut cycle time 5 minutes.
7        casting slurry temperature ****2 degree
8        body quiet stop. Time is 1.**2.5housr, temperature ****0 degree, after quiet stop body strength is 0.***0.*8Mpa
9        Steam curing cycle time, come in and out autoclave about 0.5hour, steam curing cycle time about is 6 hours/1.6Mpa, total 6.5 hours.
*0.  Cement lime fly ash style aerated block raw material proportion