SAW flux(SJ101 SJ301 SJ501)

タイトルまたは説明

Welding
Agglomerated flux

Company system: ISO***1:***8


CHARACTERISTICS for 2 hours. 
Rust, grease and moisture on the weldment should be removed before welding.



TY.SJ**1

:   
Specification: Characteristics:

TY.SJ**1 is an agglomerated calcium-silicate type welding flux

Metallurgical behavior: High silicon pick-up is obtained.When the manganese content in wire is less than 1.5%,also a manganese pick-up.

Grain size: *0 to *0 mesh  Basicity: 1.0(BIIW)

Regularly shaped welds are deposited without reducion of area or interface notches.

Slag detachability is good. A short slag is produced,thus allowing circumferential welding on small-diameter workpieces without the risk of uncontrolled slag.

The production of large pipes(especially spiral pipe welding) is a typical application fo this flux

Relatively high manganese pick-up is obtained,thus allowing the flux to be used with wires with a low Mn content.


Damp flux should be re-dried at ******0 ºC for 2 hours.Rust,grease and moisture on the weldment should be removed before welding.
TY.SJ**1

Equivalent to Lincoln **0 welding flux

EN**0 SA AR 1 *8 AC H5                        
AWS A5.*7 F7A*-EL*2 F7A*-EM*2K
 
APPLICATIONS:
Butt and flat fillet welding of 
Miniature LPG tanks, ships, vehicles, agricultural implements, machinery, boilers, Pressure vessles,bridges, structural steels.
 
CHARACTERISTICS:

1.TY-SJ**1 is an agglomerated aluminate- rutile type flux.

2. Metallurgical behavior: High silicon and manganese pick- up is obtained.

3. Grain size: *4 to *0 mesh.Basicity: 0.7( BIIW).

4. The welding performance is excellent. 
Slag detachability is very good, especially at high speed.
Welding porosity scarcely occur.

5. Its welding speed can travel up to **0 cm/ min. It is particularly useful for welding tube- web- tube joints of finned tubes.

6.TY-SJ**1 is useful for welding thin plate in single pass and limited pass.

7.The flux has low moisture pick-up  and granular stability . As the bulk density is low so is the consumption rate.

for 2 hours.
2.Rust, grease and moisture on the weldment should be removed before welding. 
 
CHEMICAL COMPOSITION OF SJ**1 

2+TiOCaFAI3+MnO***0  ***0≤0.*5

  WIRE    Si              EM*2K0.**- 0.*0   

Kraft bag with anti-moisture plastic lining inside.

*5kg/bag,  *0bags/Plywood pallet,  *4 pallets in *0'GP container,size:*4 CBM
TY.SJ**1 for  LPG cylinder welding
Smooth welding bead, slag detachability  !